作者gamer ()
站内Mechanical
标题Re: [请益] 拉伸试验的拉伸速率?
时间Thu Aug 26 04:55:15 2010
※ 引述《shoppinglin (瞎拼)》之铭言：
: 7.6.3 Speed of Testing When Determining Yield Properties—
测Yield properties的方法
: Unless otherwise specified, any convenient speed
: of testing may be used up to one half the specified minimum
: yield strength or up to one quarter of the specified minimum
: tensile strength, whichever is smaller.
除非有其他规定，任何便捷的试验速率可以以1/2的额定最
小降伏强度或1/4额定最小拉伸强度两者之较小者最为上限。
: The speed above this point shall be within the specified limits.
如果速率高於上述值，应在特定限制范围内。
: If different speed limitations are required for use in determining
: yield strength,yield point elongation, tensile strength, elongation,
: and reduction of area, they should be stated in the product specifications.
如果必须使用不同的速率限制来决定降伏强度、降伏伸长
率、拉伸强度、最大伸长率和断面收缩量，应该明确规范於产
品规格表中。
: In all cases, the speed of testing shall be such that the forces
: and strains used in obtaining the test results are accurately indicated.
: Determination of mechanical properties for comparison
: of product properties against a specification value should
: be run using the same control method and rate used to
: determine the specification value.
在所有状况下，用来取得试验结果的速率应当准确的指出
其使用之力量和应变。比较产品和规格表上的机械性质时，应
使用相同的控制方法和速率得到之值。
: 7.6.3.2 Control Method B - Rate of Straining Control
控制方法B - 应变率控制
: Method for Determining Yield Properties —
: In this method, the testing machine shall be operated in
: closed-loop control using the extensometer signal.
: The rate of straining shall be set and
: maintained at 0.015正负0.006 mm/mm/min [in./in./min].
用来量测降伏性质的方法：如果要使用此方法，试验机台
应具备含应变计讯号的封闭回路控制功能。试验的应变率应设
定维持在0.015±0.006 mm/mm/min (in./in./min)的应变率。
: NOTE 23—A Rate of Straining at 0.005 mm/mm/min [in./in./min] is
: often required for aerospace, high-temperature alloys, and titanium
: applications and when specified, must be followed rather than the
: requirement above.
附注23：在航太用、高温合金和钛合金上较常使用
0.005 mm/mm/min (in./in./min)的应变率，如果在这种情况
下，则不必遵循上述要求。
: 7.6.3.3 Control Method C—-Crosshead Speed Control
控制方法C - 夹头速率控制
: Method for Determining Yield Properties–
: The testing machine shall be set to a crosshead speed equal
: to 0.015正负0.003 mm/mm/min [in./in./min] of the original reduced section
用来量测降伏性质的方法：试验的应变率应设定维持在
0.015±0.003 mm/mm/min (in./in./min)的应变率。
: 7.6.4 Speed of Testing When Determining Tensile
: Strength—
量测拉伸强度的试验速率
: In the absence of any specified limitations on speed of testing,
: the following general rules shall apply for materials with expected
: elongations greater than 5 %.
在缺乏任何试验速率规范限制的状下，下述通用规范应用
於预期伸长率大於5%的材料上。
: When determining only the tensile strength, or after the yield behavior
: has been recorded, the speed of the testing machine shall be set between
: 0.05 and 0.5 mm/mm [or in./in.] of the length of the reduced section
: (or distance between the grips for specimens not havinga reduced section)
: per minute.
如果仅仅是要谅测拉伸强度或是纪录材料降伏之後的行为，
应以材料面积缩减区域长度的（如果试件无面积缩减区域，则以
夹持长度做标准）0.05 ~ 0.5 mm/mm/min (in./in./min)伸长率
做为试验速率区间。
--
有些地方翻得怪怪的，加减看吧。
--
※ 发信站: 批踢踢实业坊(ptt.cc)
◆ From: 220.136.41.175
1F：推 shoppinglin:谢谢 我想5%那边应该是指对(预期)伸长率超过5%的材料? 08/26 06:02
2F：→ shoppinglin:不过我主要问题还是对於速率的选择 所以应该是0.015? 08/26 06:04
3F：→ gamer:同上面所说，看你是要量测yield以前的行为，还是yield以後的 08/26 15:47
4F：→ gamer:行为，如果是前者最好使用较慢的速率(0.015)，如果是後者则 08/26 15:48
5F：→ gamer:可以快一点。 08/26 15:48
※ 编辑: gamer 来自: 220.136.65.92 (08/26 15:53)
6F：→ gamer:一般来说，会拉伸速率越慢，量测到的机械性质会较拉伸速率快 08/26 15:55
7F：→ gamer:的来得「柔性」，如果说你的材料使用在比较没有安全考量的状 08/26 15:57
8F：→ gamer:况下，是可以考虑以较快的试验速率做量测以减少试验时间。 08/26 15:58
9F：→ shoppinglin:我是要同时给出YS UTS elongation 第一点有提要同速 08/26 19:01
10F：→ shoppinglin:加上也不知道他上面写的1/2 1/4那边指的是哪来的速率 08/26 19:01
11F：→ shoppinglin:所以搞不太懂这样到底是有规定范围还是上下限.. 08/26 19:02
12F：→ gamer:我想额外规范UTS试验速率是应该是因为拉伸速率对於材料yield 08/26 19:27
13F：→ gamer:之後的影响比较小，故特别指出如只是要纪录yield之後的行为 08/26 19:28
14F：→ gamer:可以采用此较高的速率规范，那你用较慢的速率我想应该是不会 08/26 19:29
15F：→ gamer:有什麽问题。然後他提到1/2和1/4的目的应该是要避免速率过高 08/26 19:31
16F：→ gamer:造成量测结果不准确故订立一个比较通用的上限值。 08/26 19:32