※ 引述《kairiyu (E N O U G H is enough)》之銘言： : 超導體能源聖杯破滅 LK-99非超導體 : 。科學偵探們發現，樣品電阻率急速下降，且得以部分懸浮在磁鐵上，是因為材料中有雜 質，尤其是硫化亞銅。這項結論讓LK-99作為史上首個常溫常壓超導體的希望徹底破滅。 https://www.nature.com/articles/d41586-023-02585-7 Nature 上刊登的這篇新聞，重點在於雜質硫化亞銅(Cu2S) 打破了 LK-99超導體的希望， 我截取了其中提到用實驗證明了雜質影響的論文 ---------------------------------------- On 8 August, the CAS team reported on the effects of Cu2S impurities in LK-99. “Different contents of Cu2S can be synthesized using different processes,” say s Jianlin Luo, a CAS physicist. The researchers tested two samples — the first heated in a vacuum, which resulted in 5% Cu2S content, and the second in air, wh ich gave 70% Cu2S content. 8月8日，中國科學院團隊報告了 LK-99 中 Cu2S 雜質造成的影響。中國科學院物理學家羅 建林表示 “不同含量的 Cu2S 的樣品可用不同的方法來合成”。 研究人員測試了兩個樣品 ，第一個在真空中加熱，產生 5% 的 Cu2S 含量，第二個在空氣中加熱，產生 70% 的 Cu2S 含量。 The first sample’s resistivity increased relatively smoothly as it cooled, and appeared similar to samples from other replication attempts. But the second samp le’s resistivity plunged near 112 ºC (385K) — closely matching the Korean team ’s observations. 第一個樣品的電阻率隨著溫度冷卻而相對平穩的上升，與其它復現的樣品相似。 但第二個 樣品的電阻率在 112 ºC (385K)附近時急遽下降，相當符合韓國團隊觀測的結果。 “That was the moment where I said, ‘Well, obviously, that’s what made them th ink this was a superconductor,’” says Fuhrer. “The nail in the coffin was thi s copper sulfide thing.” Fuhrer 表示“那時我就說‘顯然這就是讓他們認為是超導體的原因’”。 “copper sulfi de 就是最好的證據。” *copper sulfide 指的是硫化銅一族 ------------------------------------------------ On 14 August, a separate team, at the Max Planck Institute for Solid State Resea rch in Stuttgart, Germany, reported synthesizing pure, single crystals of LK-99. Unlike previous synthesis attempts that relied on crucibles, the researchers us ed a technique called floating zone crystal growth that allowed them to avoid in troducing sulfur into the reaction, eliminating the Cu2S impurities. 8月14日，一個來自德國馬克斯-普朗克固體研究所的獨立團隊報告說合成了 LK-99 的純淨 單晶體。 跟之前仰賴坩堝不同，研究人員使用了一種稱為floating zone crystal growth 的技術，能避免在反應中引入硫，藉此消除了雜質 Cu2S 。 The result was a transparent purple crystal — pure LK-99, or Pb8.8Cu1.2P6O25. S eparated from impurities, LK-99 is not a superconductor, but an insulator with a resistance in the millions of ohms — too high to run a standard conductivity t est. It shows minor ferromagnetism and diamagnetism, but not enough for even par tial levitation. “We therefore rule out the presence of superconductivity,” th e team concluded. 其結果是一種透明的紫色晶體-純淨的 LK-99或 Pb8.8Cu1.2P6O25。 分離雜質後，LK-99 就 不是超導體了，是個電阻高達數百萬歐姆的絕緣體，電阻太高以致於無法進行標準的電導率 測試。 它表現出輕微的鐵磁性和抗磁性但卻不足以做到部分懸浮。 團隊得出結論 “因此 ，我們排除了其超導性的存在”。 * 編輯下補上 Nature 的原文網址

※ 發信站: 批踢踢實業坊(ptt.cc), 來自: 1.162.126.102 (臺灣) ※ 文章網址: https://webptt.com/m.aspx?n=bbs/Stock/M.1692408932.A.F49.html ※ 編輯: kkm99 (1.162.126.102 臺灣), 08/19/2023 11:36:55